Стандарти за изпълнение: GB/T8162 безшевна стоманена тръба за структура, GB/T8163 безшевна стоманена тръба за транспортиране на течности. 0420D и 0420E механични свойства: якост на опън 520~680MPa,<16 service strength 2420MPa, 16mm~30mm service strength 2400, 230mm Yield strength 2380MPa Impact test Q420D minus 20C Impact energy 234, impact test Q420E minus 40C Impact energy 227 :0.20, chromium: <0.30, nickel: <0.50, copper: 0.20, nitrogen: 0.015, :0.20, aluminum, 20.015.Q420E seamless steel pipe chemical composition: carbon: 0.20, silicon: 0.50, :1.70, phosphorus: 0.025, Sulfur: 0.020, : 0.07, : 0.20, : 0.20 Chromium: <0.30, Nickel: <0.50, Copper: <0.20, Nitrogen: 0.015, : 0.20, Aluminum, 20.015. Steel refining method: Steel should be processed by electric arc furnace Refining outside the furnace or gas converter plus outside refining method. After negotiation between the supply and demand parties, other methods with higher requirements can also be used to treat refining. When the demander requires a certain refining method, it should be stated in the contract.
Метод за производство на тръби: Тръбите могат да се произвеждат и чрез непрекъснато леене, леене в матрица или горещо валцуване.
Тръбите за непрекъснато леене също трябва да отговарят на разпоредбите на YB/T 4149; горещите тръби също трябва да отговарят на разпоредбите на YB/T 5221 или YB/T 5222; формованите отлети тръби също могат да се отнасят до разпоредбите за горещи (ковани) тръби.